| 廠家(產(chǎn)地) | 臺灣長春 |
|---|---|
| 牌號 | 3015NC |
| 加工級別 | 注塑級 |
| 特性級別 | 增強級 |
| 用途級別 | 纖維 |
| 銷售方式 | 品牌經(jīng)銷 |
| 類型 | 標(biāo)準(zhǔn)料 |
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 物理性能 | 吸濕率 | 24h | ASTM D570 | 0.04 | % | |
| 玻璃纖維含量 | 15 | % | ||||
| 比重 | ASTM D792 | 1.41 | ||||
| 機械性能 | 撓曲強度 | ASTM D790 | 1500 | kg/cm2 | ||
| 撓曲模數(shù) | ASTM D790 | 50000 | kg/cm2 | |||
| 引張伸長率 | ASTM D638 | 4.0 | % | |||
| 沖擊強度 | ASTM D256 | 6.0 | kg.cm/cm | |||
| 硬度 | ASTM D785 | 90 | M | |||
| 引張強度 | ASTM D638 | 950 | kg/cm2 | |||
| 電氣性能 | 體積抵抗率 | ASTM D257 | 1015 | Ω.cm | ||
| 表面抵抗率 | ASTM D257 | 1013 | Ω | |||
| 誘電正接 | ASTM D150 | 0.001 | 60Hz | |||
| 介電常數(shù) | ASTM D150 | 3.5 | 60Hz | |||
| 絕緣破壞強度 | 2mm | ASTM D149 | 20 | KV/mm | ||
| 耐電弧性 | ASTM D495 | 120 | SEC | |||
| 熱性能 | 熔點 | DSC | 225 | ℃ | ||
| 熱變形溫度 | - | 18.6kg/cm2 | ASTM D648 | 200 | ℃ | |
| - | 4.6kg/cm2 | ASTM D648 | 220 | ℃ | ||
| 熱膨脹系數(shù) | ASTM D696 | 5 | 10-5cm/cm℃ | |||
| 耐燃性 | UL94 | HB | ||||
產(chǎn)品牌號：PBT/臺灣長春/3015NC
產(chǎn)品簡介：聚對苯二甲酸丁二醇酯.英文名polybutylene terephthalate(簡稱PBT).屬于聚酯系列.PBT工程塑料是一種熱塑性聚酯.非增強型的PBT與其它熱塑性工程塑料相比.加工性能和電性能較好.PBT玻璃化溫度低.模具溫度在50℃時即可迅速結(jié)晶.加工周期短.聚對苯二甲酸丁二醇酯(PBT)被廣泛應(yīng)用于電子.電氣和汽車工業(yè)中。
產(chǎn)品信息：PBT為乳白色半透明到不透明.結(jié)晶型熱塑性聚酯.具有高耐熱性、韌性、耐疲勞性.自潤滑.低摩擦系數(shù).耐候性.吸水率低.僅為0.1%.在潮濕環(huán)境中仍保持各種物性(包括電性能).電絕緣性.但體積電阻.介電損耗大.耐熱水.堿類.酸類.油類.但易受鹵化烴侵蝕.耐水解性差.低溫下可迅速結(jié)晶.成型性良好。
工藝條件：干燥處理：這種材料在高溫下很容易水解，因此加工前的干燥處理是很重要的。建議在空氣中的干燥條件為120℃，6~8小時，或者150℃，2~4小時。濕度必須小于0.03%。如果用吸濕干燥器干燥，建議條件為150℃，2.5小時。熔化溫度：225~275℃，建議溫度：250℃ 。模具溫度：對于未增強型的材料為40~60℃。要很好地設(shè)計模具的冷卻腔道以減小塑件的彎曲。熱量的散失一定要快而均勻。建議模具冷卻腔道的直徑為12mm。注射壓力：中等（**大到1500bar）。注射速度：應(yīng)使用盡可能快的注射速度（因為PBT的凝固很快）。流道和澆口:建議使用圓形流道以增加壓力的傳遞（經(jīng)驗公式：流道直徑=塑件厚度+1.5mm）?？梢允褂酶鞣N型式的澆口。也可以使用熱流道，但要注意防止材料的滲漏和降解。澆口直徑應(yīng)該在0.8~1.0*t之間，這里 t是塑件厚度。如果是潛入式澆口，建議**小直徑為0.75mm。